KANGAROO PLASTICS DATA
SHEET
Geomembrane Technical
Specifications-
LLDPE Smooth Geomembrane
(Metric Units)
|
Properties |
Test Method |
Frequency |
Units |
Min.
Value |
|
KPLLDS |
KPLLDS |
KPLLDS |
KPLLDS |
KPLLDS |
|
0.75 mm |
1.00 mm |
1.50 mm |
2.00 mm |
2.50 mm |
|
Thickness
Ø
Minimum Avg. Value
Ø
Lowest Individual Value |
ASTM D 5199 |
Every
Roll |
mm
mm |
0.75
0.68 |
1.00
0.90 |
1.50
1.35 |
2.00
1.80 |
2.50
2.25 |
|
Density (min. ave.) |
ASTM D 1505 |
50,000
kg |
g/cc |
0.939 |
0.939 |
0.939 |
0.939 |
0.939 |
|
Tensile
Properties¹
(min. ave.)
Ø
Strength at break
Ø
Elongation at break (gauge length 50mm) |
ASTM D 6693
Type IV
@500 mm/min. |
7,000
kg
|
kN/m
% |
20
800 |
27
800 |
40
800 |
53
800 |
66
800 |
|
2%
Modulus (Max.) |
ASTM D 5323 |
Per
Formulation |
N/mm |
370 |
420 |
630 |
840 |
1050 |
|
Tear
Resistance (min. ave.) |
ASTM D 1004 |
10,000
kg |
N |
70 |
100 |
150 |
200 |
250 |
|
Puncture Resistance (min. ave.) |
ASTM D 4833 |
10,000
kg |
N |
190 |
250 |
370 |
500 |
620 |
|
Axi –
Symetric Break Strain |
ASTM D 5617 |
Per
Formulation |
% |
30 |
30 |
30 |
30 |
30 |
|
Carbon
Black Content |
ASTM D 1603 |
7,000
kg |
% |
2.0 –
3.0 |
2.0 –
3.0 |
2.0 –
3.0 |
2.0 –
3.0 |
2.0 –
3.0 |
|
Carbon
Black Dispersion |
ASTM D 5596 |
10,000
kg |
Category |
Note 2* |
Note 2* |
Note 2* |
Note 2* |
Note 2* |
|
Oxidative Induction Time (OIT)
Ø
Standard OIT
or
Ø
High Pressure OIT |
ASTM D 3895
ASTM D 5885 |
50,000
kg
50,000
kg |
min.
min. |
100
400 |
100
400 |
100
400 |
100
400 |
100
400 |
|
Oven
Aging at 85°C
Ø
Standard OIT. % Retained after 90 days |
ASTM D 5721
ASTM D 3895 |
Per
Formulation |
% |
35 |
35 |
35 |
35 |
35 |
|
UV
Resistance
Note3*
Ø
High pressure OIT
Note4*.
% Retained after 1600 hrs |
GRI GM 11
ASTM D 5885 |
Per
Formulation |
% |
35 |
35 |
35 |
35 |
35 |
|
Seam
Properties
Ø
Shear Strength
Ø
Peel Strength - Hot Wedge
- Extrusion Fillet |
ASTM D 6392
(@ 50mm/min) |
Per
Formulation |
kN/m
kN/m
kN/m |
7.9
6.6
6 |
10.5
8.7
7.6 |
15.7
13.1
11.6 |
21
17.5
15.4 |
26.3
21.9
20 |
|
Roll Dimensions
Ø
Width
Ø
Length
Ø
Area |
|
|
meters
meters
Sq. mtrs. |
7
280
1960 |
7
210
1470 |
7
140
980 |
7
105
735 |
7
84
588 |
Note:
1.
Machine Direction (MD) and Transverse Direction (TD) average
values are on the basis of 5 specimens each direction.
Break elongation is calculated using a gauge length of 50 mm.
2.
Carbon black dispersion for 10 different
views: Nine in Categories 1 and 2 with one allowed in Category 3.
3.
The condition of the test should be 20 hr. UV
cycle at 75°C followed by 4 hr. condensation at 60°C.
4.
UV resistance is based on percent retained
value regardless of the original HP-OIT value.
This data
is provided for informational purpose only. The specifications on this
sheet are subject to change without notice.
|
Home |
Profile |
Products |
Infrastructure |
Quality Policy |
Geomembrane |
Location Map |
Careers |
Contact Us
|
Kangaroo Plastics Middle East L.L.C. | Tel:
971-4-8804700 | Fax: 971-4-8804702 |
Email |
This website © Kangaroo Plastics
Middle East L.L.C. All rights reserved.
|